Abstract

We have prepared nanometer-sized CoPt particles dispersed in a poly~methyl methacrylate~PMMA!matrix, as a novel nanostructured magnetic plastic, through a soft chemical processing route. In this work, CoPt nanoparticles were successfully synthesized from a solution phase reduction system in the presence of capping ligands and stabilizing agents at high temperature. The CoPt nanoparticles were annealed at 400 °C for 3 h, and were subsequently re-dispersed inmethylmethacrylate~monomer! . The polymerization was induced by a UV source and the hardness of final product was adjusted by varying the amount of monomeric cross-link agent. Annealed bare CoPt nanoparticles as a ‘‘core’’ material and CoPt–PMMA composite material were characterized by using energy dispersive spectroscopy, transmission electron microscopy, and x-ray diffraction, indicating that we are able to prepare CoPt nanoparticles with 10 nm in diameter ~after annealing by employing this high temperature colloidal processing method. Magnetic investigation of this CoPt–PMMA material indicates an intrinsic coercivity of 300 Oe at 300 K and 1665 Oe at 5 K.

Journal Name

J. Appl. Phys.

Download

Share

COinS